Abstract

The microstructure and mechanical properties of hot-pressed Al_2O_3/Cu composites with a different sintering temperature have been studied. The size of matrix grain and Cu dispersion in composites increased with increase in sintering temperature. Fracture toughness of the composite sintered at high temperature exhibited an enhanced value. The toughness increase was explained by the thermal residual stress, crack bridging and crack branching by the formation of microcrack. The nanocomposite, hot-pressed at 1450°C, showed the maximum fracture strength of 707 MPa. The strengthening was mainly attributed to the refinement of matrix grains and the increased toughness.

• Keywords: Al_2O_3/Cu nanocomposites;Sintering temperature;Microstructure;Mechanical properties;;